Influence of nanosized particles on physical and mechanical properties of galvanic zinc coating
DOI:
https://doi.org/10.28983/asj.y2023i7pp159-165Keywords:
nanocomposite coating, galvanic zinc plating, nanosized particles, aluminum oxide, microhardness, wear resistanceAbstract
The article presents the results of a study of microhardness and wear resistance of electroplated coatings based on zinc, with the inclusion of Al2O3 nanosized particles in the composition. It has been established that when nano-sized powders are introduced into galvanizing electrolytes, there is a change in microhardness and wear resistance. Thus, when adding from 1 to 9 g/l of Al2O3 nanosized materials to the electrolyte, the microhardness of the resulting coating increased by 10–65%. The best results were obtained for the coating modified with nanosized particles with a concentration of 5 g/l - 657 HV units. Wear resistance tests showed that the total wear of specimens coated with nanocomposite galvanized zinc is 1.5–1.7 times less than that of specimens coated without adding nanosized aluminum oxide particles to the electrolyte.
Downloads
References
Ачкасов К. А. Прогрессивные способы ремонта сельскохозяйственной техники. 2-е изд., перераб. и доп. М.: Колос, 1992. 271 с.
Бородин И. Н. Упрочнение деталей композиционными покрытиями. М.: Машиностроение, 1982. 141 с.
Результаты стендовых испытаний гидрораспределителей, восстановленных с применением нанокомпозиционного гальванического железнения / В. В. Сафонов [и др.] // Научная жизнь. 2019. № 2. С. 43-50.
Сайфуллин, Р. С. Неорганические композиционные материалы. М. : Химия, 1983. 304 с.
Сафонов В. В., Шишурин С. А., Семочкин В. С. Наномодифицированные химические покрытия с улучшенными физико-механическими свойствами // Инновации в АПК: проблемы и перспективы. 2014. № 3 (3). С. 18-22.
Седиментационная стойкость электролита-суспензии и микротвердость нанокомпозиционных гальванических покрытий на основе хрома / В. В. Сафонов [и др.] // Научная жизнь. 2021. Т. 16. № 1. С. 65-76.
Технология упрочнения и восстановления деталей сельскохозяйственной техники нанокомпозиционным гальваническим железнением / В. В. Сафонов [и др.] // Научная жизнь. 2019. № 2. С. 33-42.
Шишурин С. А., Семочкин В. С., В Сафонов. В., А Гурьев. Е. Структура и физико-механические свойства композиционных гальванохимических покрытий // Вестник АПК Ставрополья. 2014. № 3 (15). С. 77-80.
Application of Composite Electroless Nickel Coatings on Precision Parts of Hydraulics Aggregates / V. Safonov [et al.] // Tribology in Industry. 2019. Vol. 41. No. 1. P. 14-22.
Investigation of Structure and Wear Resistance of Nanocomposite Coating of Chemical Nickel / V. Safonov [et al.] // Tribology in Industry. 2018. Vol. 40. No. 4. P. 529-537.
Safonov V.V., Shishurin S. A., Semochkin V. S., Zakharevich A. M. Effect of alumina nanoparticles on the structure and physicochemical properties of chromium coatings // Surface Engineering and Applied Electrochemistry. 2015. Vol. 51. No 6. P. 517-522.
The Influence of Nanosized Materials on Microhardness of Iron-Based Electroplating / V. Safonov [et al.] // International Journal of Innovative Technology and Exploring Engineering. 2019. Vol. 8. No. 6. P. 629-632.
Downloads
Published
Issue
Section
License
Copyright (c) 2023 The Agrarian Scientific Journal
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.