Operational properties of chromium coatings obtained from self-regulating electrolyte with addition of nano-dimensional particles
DOI:
https://doi.org/10.28983/asj.y2019i7pp95-100Keywords:
composite coatings, nanoscale particles, electroplating, microhardness, wear resistanceAbstract
The article presents the results of laboratory studies of microhardness and wear resistance of basic and nanocomposite electroplating chromium coatings. The most effective strengthening phase was chosen - nanosized alumina powder at a concentration of 3 g / l. The use of nano-sized aluminum oxide powder makes it possible to increase the microhardness and wear resistance of nanocomposite coatings by 1.5-1.8 times as compared to the base ones.
Downloads
Download data is not yet available.
References
Проведенные лабораторные исследования позволили определить наноразмерный материал – оксид алюминия, позволяющий получать покрытия с повышенными значениями микротвердости. Микротвердость нанокомпозиционных покрытий полученных при концентрации в электролите наноразмерных частиц оксида алюминия 3 г/л в 1,47 раза выше микротвердости базовых хромовых покрытий. В результате проведенных лабораторных испытаний на износостойкость установлено, что нанокомпозиционные электролитические покрытия на основе хрома обладают износостойкостью в 1,5-1,8 раза выше износостойкости базовых покрытий хрома и в 2,1-2,2 раза выше износостойкости стали ШХ15. Данные покрытия следует рекомендовать для восстановления и упрочнения ресурсоопределяющих деталей агрегатов сельскохозяйственной техники.